Example, in EN 10269, ASTM F2281 and in ASTM A 320/A 320M. Cross-sectional area of machined test piece after fracture, mm2. Percentage reduction of.
Cozdemir,I typed DIN 1691 into the Search box at Global. The following links shows that the standard has been superceded by DIN EN 1561:=ugwuegbuchima,ASTM A 536 is a standard for ductile iron, which is different from grey iron. Also, E standards from ASTM are for testing and evaluation techniques, not for specifying products by material composition, mechanical properties, etc. In this case, it is a standard for compression testing, which is a test that is performed on cast irons (ductile iron, grey iron, etc.). RE: ASTM Equivalent to DIN 1691 GG25.